At the same time as the development of organic friction materials, another type of friction material that is more commonly used is powder metallurgy friction materials. Before 1929, the Soviet Union's Schwarzkopf applied for the first patent for a sintered material for friction. The material was an alloy containing a small amount of lead, tin and copper. The United States also started the research of this work in 1929. In the late 1930s, the material was first used on the clutch plates of D-7 and D-8 scrapers. The American General Company organized the production of sintered materials for clutch plates in 1932, which was adopted by the aviation industry at that time.
Toz metalurjisi sürtünme malzemeleri alanındaki daha olgun temel işlem ilkesi, 1937-1941 yılları arasında Willman ve meslektaşları tarafından Amerika Birleşik Devletleri'nde elde edilen patentlerde somutlaştırılmıştır. Bu patent, sürtünme malzemesinin metal matrisi olarak kalay bronzu kullanır ve kalay bronz çinko ile alaşımlanabilir. Sürtünme katsayısını artırmak için demir ve silika eklenir ve yağlama bileşenleri olarak grafit ve kurşun eklenir.
1950-1980 arasındaki yaklaşık bir süre zarfında, toz metalurjisi sürtünme malzemeleri, kuru sürtünme ve ıslak sürtünme iş yerlerinde başarıyla kullanıldı. Uygulama alanları, orta ve ağır araçlar, tarım makineleri vb. için fren ve debriyajlara kadar genişletildi. 1958'den beri, British Frood Company, Amerikan SK Wellman Company ve Bendix Aviation ile bronz-tabanlı, demir{ üretmek için işbirliği yaptı. {4}}tabanlı ve seramik bazlı sürtünme malzemeleri.